TECHNYL STAR™ S 218 V30 BLACK 31 N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL STAR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0EY2oz_TECHNYL-STAR-S-218-V30-BLACK-31-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYLSTAR™ S 218 V30 Black 31N is based on a patented high flow polyamide 6 resin (TechnylStar), heat stabilized, reinforced with 30% of glass fibre, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.65 | -- | % | |
| Flow | 0.35 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.95 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.540 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9600 | 6200 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 190 | 110 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.8 | 4.5 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 8650 | 4750 | MPa | ASTM D790 |
| -- | 8400 | 4900 | MPa | ISO 178 |
| Flexural Strength | 255 | 140 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 32 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 81 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| -30°C | 12 | -- | J/m | ASTM D256 |
| -30°C | 12 | 14 | kJ/m² | ISO 180/1A |
| 23°C | 12 | 21 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 205 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 240 | °C | |
| Front Temperature | 240 to 245 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melinex® 442 | DuPont Teijin Films U.S. | Polyester, TP | Melinex® |
| Anjaflam® 050/85S-FR | Almaak International GmbH | PC+ABS | Anjaflam® |
| FHR Polypropylene P9M7R-056 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| IPC PP 4830C-C | International Polymers Corporation | PP Copolymer | IPC PP |
| LUVOCOM® 1200-8777 | Lehmann & Voss & Co. | ABS | LUVOCOM® |