Karina WHITE PVC COMPOUND 105905-10/ 96-BY-IS-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0DOG1p_Karina-WHITE-PVC-COMPOUND-105905-10-96-BY-IS-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ECONOMIC HEAVY METAL FREE PVC COMPOUND CLASS 105C (PVC/EB) RECOMMENDED FOR INSULATION OF ELECTRICAL WIRES FOR ELECTRICAL EQUIPAMENTS. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.31 to 1.37 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | < 50 | ppm | ASTM D1971 |
| Chromium Content | < 100 | ppm | ASTM D1971 |
| Color | OK | ME 12 | |
| Color a | -2.05 to 0.950 | ME 12 | |
| Color b | -0.630 to 2.37 | ME 12 | |
| Color L | 81.6 to 84.6 | ME 12 | |
| Mercury Content | < 100 | ppm | ASTM D1971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | ASTM D1971 |
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 86 to 90 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 130 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 130 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | NBR 5403 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 136°C |
| 3 . | Aged in Air for 168 hr at 136°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EcoLon® MRGF1518-BK | Wellman Engineering Resins | Nylon 66 | EcoLon® |
| Karina GRAY PVC COMPOUND 807D18/473-D-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® SR3108FM | LG Chem Ltd. | PC | Lupoy® |
| REV Materials 8008-003 | REV Materials | PP, Unspecified | REV Materials |
| TOTAL Polyethylene Bio TPSeal® 0850_05 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |