Matrixx 80S7351
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | The Matrixx Group, Inc. |
| Trademark: | Matrixx |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0AhCBN_Matrixx-80S7351.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Matrixx 80S7351 is a Polyethylene Terephthalate (PET) material filled with 35% glass fiber. It is available in North America. Primary attribute of Matrixx 80S7351: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, 3.18 mm) | 159 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 3.18 mm) | 9650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 236 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 210 | °C | |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 35 | % | ASTM D5630 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Elastollan® B 64 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Grilamid® XE 4176 black 9288 | EMS-GRIVORY | Nylon 1010 | Grilamid® |
| Hapflex™ 871-4 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Honeywell PCTFE P2000HS | Honeywell | PCTFE | Honeywell PCTFE |
| POLYCOMPO PE ACE30N | POLYCOMPO Co.,Ltd. | LDPE | POLYCOMPO PE |