LNP™ LUBRILOY™ UX98388 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0AEEG6_LNP-LUBRILOY-UX98388-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* UX98388 is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRILOY* Compound PDX-U-98388 Product reorder name: UX98388 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 2.5 | % | Internal Method |
| Across Flow : 24 hr | 1.6 | % | ISO 294-4 |
| Flow : 24 hr | 1.6 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.34 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 72.0 | MPa | ISO 527-2 |
| Yield | 78.0 | MPa | ISO 527-2/5 |
| Break | 67.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 6.1 | % | ISO 527-2/5 |
| Flexural Modulus | ISO 178 | ||
| -- | 2500 | MPa | |
| -- 1 | 2400 | MPa | |
| Flexural Stress | 106 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(0.45 MPa, Unannealed, 64.0 mm Span) | 131 | °C | ISO 75-2/Bf |
| CLTE - Transverse (23 to 60°C) | 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALECCA K-200 | Denka Company Limited | ABS | MALECCA |
| NatureFlex™ 165 NE | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Braskem PP CP 145 | Braskem | PP Impact Copolymer | Braskem PP |
| LNP™ LUBRICOMP™ UL002S compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |
| POLYFORM C 2,5 | POLYMA Kunststoff GmbH & Co. KG | Acetal (POM) Homopolymer | POLYFORM |