UBE Nylon 1015GC6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBE Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 09x9X1_UBE-Nylon-1015GC6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UBE Nylon 1015GC6 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.70 | -- | % | ASTM D955 |
| Water Absorption (Saturation) | 6.6 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 100 | -- | ||
| R-Scale | 120 | 110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 167 | 98.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.0 | 6.0 | % | ASTM D638 |
| Flexural Modulus | 7840 | 4410 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 245 | 127 | MPa | ASTM D790 |
| Compressive Strength | 27.4 | 15.7 | MPa | ASTM D695 |
| Shear Strength | 85.2 | 58.8 | MPa | ASTM D732 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -30°C | 78 | 140 | J/m | |
| 23°C | 110 | 230 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 215 | -- | °C | ASTM D648 |
| Melting Temperature | 215 to 225 | -- | °C | |
| CLTE - Flow | 2.5E-5 | -- | cm/cm/°C | ASTM D696 |
| RTI Elec (0.794 mm) | 65.0 | -- | °C | UL 746 |
| RTI Imp (0.794 mm) | 65.0 | -- | °C | UL 746 |
| RTI Str (0.794 mm) | 65.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | |||
| 60 Hz | 4.20 | -- | ||
| 1 MHz | 3.80 | -- | ||
| Dissipation Factor | ASTM D150 | |||
| 60 Hz | 0.010 | -- | ||
| 1 MHz | 0.020 | -- | ||
| Arc Resistance (0.794 mm) | 121 | -- | sec | ASTM D495 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.794 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 240 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 275 | °C | |
| Nozzle Temperature | 275 | °C | |
| Processing (Melt) Temp | 285 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Pressure | 83.2 | MPa | |
| Back Pressure | 9.80 | MPa | |
| Screw Speed | 100 to 130 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RODRUN LC-5030GN | UNITIKA Plastics Division | LCP | RODRUN |
| SEQUEL® 1828 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Unichem 8012N-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Iupital® TC3030 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| LNP™ STAT-KON™ DD0009E compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |