RTP 705 CC UV
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 09g6tR_RTP-705-CC-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5520 | MPa | ASTM D638 |
| Tensile Strength | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 129 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 121 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 3mil/in.Tensile Elongation, ASTM D-638: 4-6% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 177 - 288 | °C | |
| Middle Temperature | 177 - 288 | °C | |
| Front Temperature | 177 - 288 | °C | |
| Mold Temperature | 23.9 - 51.7 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP LGF 30 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| FHR Polypropylene P5C4K-089 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Huafon JF-S-8030A | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LNP™ LUBRICOMP™ YP003 compound | SABIC Innovative Plastics | TPEE | LNP™ LUBRICOMP™ |
| Sylvin 5132-90UV Clear 8371 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |