Lupolen 5031 L Q 449 K
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 094wa5_Lupolen-5031-L-Q-449-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupolen 5031 L Q 449 K is a high density polyethylene (HDPE) base material for extrusion of silane crosslinked pipes (PE-Xb). It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 13 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 62 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 50.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 10 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 125 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 131 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 280 | °C |
| Extrusion instructions |
|---|
| Melt temperatures above 280 °C should be avoided to prevent potential degradation. In case higher temperatures are needed please contact LyondellBasell. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R533H01 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Chemlon® 225 G | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| HIPOLEN P® MA 41 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| Sylvin 9077-90C LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ CFR7630 resin | SABIC Innovative Plastics | PC | LEXAN™ |