Jam 22502AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Jam Petrochemical Company |
| Trademark: | Jam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 081l1T_Jam22502AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
22302 is a LLDPE blown film grade designed for applications requiring ease of processing and good optical properties even at low extrusion temperature. This resin is well suited for blending with LDPE and for general pupose uses, including agricultural applications. Features
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness | 12.0 - 150 | µm |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 25 µm, blown film | 175 | MPa | ASTM D882 |
| 2% secant, TD : 25 µm, blown film | 220 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 11.5 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 40.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 32.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 600 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 130 | g | ASTM D1922 |
| TD : 25 µm, blown film | 350 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 38 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 21 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB40 GR45 NL HS | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Sumitomo Epoxy TEM 9053C | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| ALCUDIA® LDPE 2625FG | REPSOL | LDPE | ALCUDIA® LDPE |
| Axiall PVC 9175 Blue 90 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Sylvin 8950-50FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |