LNP™ STAT-KON™ MFD03 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 07A4pi_LNP-STAT-KON-MFD03-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON MFD03 is a compound based on Polypropylene resin containing 15% Glass Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound MF-15 Product reorder name: MFD03 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.0 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.92 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3310 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 34.5 | MPa | ASTM D638 |
| Yield | 34.0 | MPa | ISO 527-2 |
| Break | 16.5 | MPa | ASTM D638 |
| Break | 15.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.7 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2 |
| Break | 6.9 | % | ASTM D638 |
| Break | 5.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Stress | 51.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D256 |
| 23°C 2 | 23 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D4812 |
| 23°C 3 | 13 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.2 | J | ASTM D3763 |
| -- | 5.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 147 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 142 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 98.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE CC253 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| ALTECH® PA6 C 4240/106 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| POLYfill PPHC K2040H | Polykemi AB | PP, Unspecified | POLYfill |
| SQUARE® SSR1501-45A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |
| Akulon® FC-X9201 | DSM Engineering Plastics | Nylon 6 | Akulon® |