DynaStat® 457
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Polymer Dynamix |
| Trademark: | DynaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0750n5_DynaStat-457.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Antistatic Polyethylene Compound Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 - 0.960 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 20.7 | MPa | ASTM D638 |
| Fracture | 17.2 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 24 | % | ASTM D638 |
| Fracture | > 50 | % | ASTM D638 |
| Flexural Modulus | 703 | MPa | ASTM D790 |
| Flexural Strength | 24.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 130 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 - 1.0E+8 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+6 - 1.0E+8 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 188 - 196 | °C | |
| Middle Temperature | 193 - 202 | °C | |
| Front Temperature | 199 - 210 | °C | |
| Nozzle Temperature | 202 - 213 | °C | |
| Processing (Melt) Temp | 210 - 216 | °C | |
| Mold Temperature | 26.7 - 60.0 | °C | |
| Injection Pressure | 34.5 - 55.2 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 399 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 188 - 196 | °C | |
| Cylinder Zone 3 Temp. | 193 - 202 | °C | |
| Cylinder Zone 5 Temp. | 199 - 210 | °C | |
| Melt Temperature | 204 - 216 | °C | |
| Die Temperature | 199 - 216 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 25 to 100 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1035-70UV | Teknor Apex Company | TPE | Telcar® |
| ASI POLYETHYLENE CLP 855-01 Natural | A. Schulman Inc. | LLDPE | ASI POLYETHYLENE |
| Cri-Line SP-918 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Halar® 6014F | Solvay Specialty Polymers | ECTFE | Halar® |
| LNP™ THERMOCOMP™ Noryl_FM4025 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ THERMOCOMP™ |