Ghaed ABS/PC GAC 250
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed ABS/PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 06tPD3_Ghaed-ABS-PC-GAC-250.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS Alloy : Non Reinforced Grade Classification: General purpose>Injection grade Characteristic: Injection grade, high impact Resistance Application GAC 250 resin gives exceptional impact strength even at low temperature and has a high heat resistance. Typical applications include automotive instrument panel, automotive interior and exteriortrim. Electrical and Electronic component and etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/21.6 kg) | 45 to 55 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 to 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 51.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | > 80 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | > 1860 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | > 76.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5 | > 40 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 115 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 6.4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYMAX® GT4402 | Westlake Chemical Corporation | LLDPE | TYMAX® |
| Witcom PP 2012/077 Blue | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| YUNGSOX® PP 3084 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| DILAMID® 66 FVT 30 BLACK | Dilaplast S.p.A. | Nylon 66 | DILAMID® |
| Iupilon® GS2030MN1 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |