AIE PA6 50G3F
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 05cpby_AIE-PA6-50G3F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AIE PA6 50G3F is a polyamide 6 (nylon 6) material, which contains a filler of 15% glass fabric reinforcement. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of AIE PA6 50G3F are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 - 0.80 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 207 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 220 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 245 - 260 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Mold Temperature | 50.0 - 110 | °C | |
| Injection Pressure | 30.0 - 80.0 | MPa | |
| Holding Pressure | 40.0 - 50.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Cylinder Temperature 4: 230 to 245°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 12 MO | Röchling Sustaplast SE & Co. KG | Nylon 12 | SUSTAMID |
| Badaflex® TPE-S 60D 1160 | Bada AG | SEBS | Badaflex® |
| Alpha PVC GW 2326-A-VW1 NAT LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| FHR EPS 54-5354 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| POCAN® KU 1-7313 000000 | LANXESS GmbH | PBT+PET | POCAN® |