TAROLOX 111 G8
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 05CGQn_TAROLOX-111-G8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET medium viscosity 40% glass fibres reinforced, very good chemical resistance, good mechanical, thermal and electrical properties, low moisture absorption, good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 to 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.40 to 0.60 | % | |
| Flow | 0.15 to 0.30 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Granule Humidity 1 | < 0.030 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(750°C) | 40 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 185 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 12500 | MPa | ISO 178 |
| Flexural Stress 4 | 265 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 230 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 242 | °C | ISO 306/B50 |
| Ball Pressure Test (245°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 256 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (1.00 mm) | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 6 | < 100 | mm/min | ISO 3795 |
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 90.0 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | US FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 506P | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| TEKALOY™ G70A3 | Mando Advanced Materials Co., Ltd. | PC+ABS | TEKALOY™ |
| Delta PBR-2G30 | Delta Polymers | PBT | Delta |
| Devcon Korrobond 95 | Devcon | Epoxy | Devcon |
| DuraElast 1730-71 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraElast |