ASTALOY™ PC/ABS MT7228HF
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 04rRwP_ASTALOY-PC-ABS-MT7228HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ABS MT7228HF is a high melt flow, high heat resistance and high impact strength alloy of Polycarbonate & ABS which has been designed for injection moulding applications requiring a balance of exceptional impact toughness (especially at low temperatures), high product rigidity and a high heat resistance whilst maintaining easy processing and ease of decorative painting. Note: The last letter U indicates additional UV stabilisation has been added [ ie: ASTALOY™ PC/ABS MT7228HFU]. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/3.8 kg | 10 | g/10 min | |
| 260°C/5.0 kg | 24 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 56.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 150 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 92.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.50 mm) | 680 | J/m | ASTM D256 |
| Gardner Impact (3.50 mm) | 65.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 112 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 117 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 122 | °C | |
| Vicat Softening Temperature | 143 | °C | ASTM D1525 5 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 255 to 275 | °C | |
| Front Temperature | 265 to 285 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tempalux® 20% GF | Westlake Plastics Company | PEI | Tempalux® |
| SKYGREEN® K2012 | SK Chemicals | PETG | SKYGREEN® |
| NYLOY® KF-0010N 2140B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| MAJORIS GFR307 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| SQUARE® LSR8610-10A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |