Xuchuan A-9000/B-6088
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 04ql4d_Xuchuan-A-9000-B-6088.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Xuchuan A-9000/B-6088 is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) product. It is available in Asia Pacific. Typical application: Consumer Goods. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.400 to 0.480 | g/cm³ | |
| Density | |||
| A-9000 : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-6088 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-9000 : 40°C | 1.20 to 1.80 | Pa·s | |
| B-6088 : 40°C | 0.600 to 0.800 | Pa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Ross Flex (23°C) 1 | No Crack |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 6.0 to 8.0 | sec | |
| End of Rise Time | 25.0 to 30.0 | sec |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 180 to 250 | kg/m³ | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 50 to 60 | °C | |
| Preheat Time | |||
| Part A | 6.0 to 8.0 | hr | |
| Part B | 6.0 to 8.0 | hr | |
| Processing Temperature | |||
| Part A | 40 to 45 | °C | |
| Part B | 38 to 42 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 to 80 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 4.20 to 6.90 | MPa | |
| Tensile Elongation (Break) | 360 to 450 | % | |
| Tear Strength | 18.0 to 27.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 83 to 85 | ||
| Demold Time | 5.0 to 7.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 55.0 to 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | 40000 cycles, Break length 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5003S1 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Niche PA66GF33BK | Niche Polymer, LLC | Nylon 66 | Niche |
| NEFTEKHIM PS 409M | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| PERCOM® KHS09 | A. Schulman Europe | PP Homopolymer | PERCOM® |
| DOW™ LDPE 505I | The Dow Chemical Company | LDPE | 陶氏低密度聚乙烯 |