POCAN® B 4239 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Corporation |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 04d3Km_POCAN-B-4239-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 30 % glass fibers, injection molding, flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.67 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 37.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 250°C, 2.00 mm 1 | 0.90 | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.10 | % | |
| Flow : 250°C, 2.00 mm 3 | 0.30 | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 186 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 10100 | MPa | ASTM D638 |
| 23°C | 11500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break, 23°C | 119 | MPa | ASTM D638 |
| Break, 23°C | 125 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break, 23°C | 2.2 | % | ASTM D638 |
| Break, 23°C | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 23°C | 8360 | MPa | ASTM D790 |
| 23°C 5 | 10500 | MPa | ISO 178/A |
| Flexural Strength | |||
| 23°C | 199 | MPa | ASTM D790 |
| 23°C 6 | 200 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength (23°C) 7 | 2.6 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halving Interval | IEC 60216 | ||
| -- 8 | 8.4 | °C | |
| -- 9 | 12.0 | °C | |
| -- 10 | 9.3 | °C | |
| Temperature Index 11 | IEC 60216 | ||
| Electric Strength | 145 | ||
| Tensile Impact Strength | 130 | ||
| Tensile Strength | 155 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion | A/B 1 | IEC 60426 | |
| ISO Shortname | PBT, GFHMR, 09-110, GF30; ISO 1043-PBT GF FR (17) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | ||
| -- 12 | 2.10 | J | |
| -- 13 | 2.30 | J | |
| Film Puncture Force | ISO 6603-2 | ||
| -- 14 | 649 | N | |
| -- 15 | 669 | N |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| Ball Pressure Test (213°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 16 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 2.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.24 | W/m/K | ISO 8302 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (23°C, 1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.90 | ||
| 23°C, 1 MHz | 3.80 | ||
| Comparative Tracking Index (Solution A) | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-0 | ||
| 0.800 mm | V-0 | ||
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 725 | °C | |
| 1.60 mm | 725 | °C | |
| 3.00 mm | 725 | °C | |
| Oxygen Index 17 | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; WZ 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; WZ 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | Tensile Impact Strength |
| 9 . | Electric Strength |
| 10 . | Tensile Strength |
| 11 . | 20000 h |
| 12 . | -30°C |
| 13 . | 23°C |
| 14 . | -30°C |
| 15 . | 23°C |
| 16 . | 10°C/min |
| 17 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® 233 GH | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Gravi-Tech™ GT6200-5002 X4 Black | PolyOne Corporation | Nylon 12 | Gravi-Tech™ |
| Sylvin 5210-75 White 1553 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALTECH® PC ECO 1000/141 FR IM | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| SABIC® LLDPE MG200024 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |