LNP™ THERMOCOMP™ LC004XXP compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 04M9xd_LNP-THERMOCOMP-LC004XXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LC004XXP is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features include; Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound LC-1004 NAT Product reorder name: LC004XXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 199 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 13900 | MPa | ISO 178 |
| Flexural Stress | 280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 45 | kJ/m² | ISO 180/1U |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 to 360 | °C | |
| Middle Temperature | 366 to 377 | °C | |
| Front Temperature | 382 to 393 | °C | |
| Processing (Melt) Temp | 382 to 388 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Talcoprene® 1522SMT NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Vi-Chem PVC VNC100E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Arak LLDPE LL0220CA | Shazand (Arak) Petrochemical Corporation | LLDPE | Arak LLDPE |
| Hyundai EP PA6 LS630 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| PENTAMID A GV30 H yellow 1018/1 | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |