LNP™ LUBRICOMP™ RFL36S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 047sCg_LNP-LUBRICOMP-RFL36S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound RFL-4036 HS Product reorder name: RFL36S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 139 | MPa | ASTM D638 |
| Break | 138 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 9700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 237 | MPa | ASTM D790 |
| -- | 211 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.58 | ASTM D3702 Modified | |
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.6 | J | ASTM D3763 |
| -- | 2.89 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | |||
| Flow : -40 to 40°C | 3.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SolVin 367NF | INOVYN | PVC, Unspecified | SolVin |
| Nylene® 8100 | Custom Resins Group | Nylon 612 | Nylene® |
| OnForce™ LFT LF6600-5018 X2 NHFR BLACK | PolyOne Corporation | Nylon 66 | OnForce™ LFT |
| Softell TKG 300N 1 G22843 | LyondellBasell Industries | PP Copolymer | Softell |
| Hostacom X M3 T15 305590 | LyondellBasell Industries | PP Copolymer | Hostacom |