TIPELIN® BB 620-17
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 03VPTd_TIPELIN-BB-620-17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN BB 620-17 is a high density polyethylene copolymer (with hexen-1 as comonomer) grade for blow moulding of products which require high rigidity. The grade contains antioxidant and acid scavenger TIPELIN BB 620-17 is recommended for small size bottles for food packing (for dairy products, yogurt, mineral water, juice). The product is suitable for injection moulding of small size containers for food applications. Furthermore it is suitable for corrugated pipes too TIPELIN BB 620-17 is suitable for food contact, for manufacturing of pharmaceutical packing products and toys. The product complies with Food Contact, Pharmaceutical and Toy Safety Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.70 | g/10 min | |
| 190°C/21.6 kg | 50 | g/10 min | |
| 190°C/5.0 kg | 2.9 | g/10 min | |
| Environmental Stress-Cracking Resistance (100% Igepal CO-630, Injection Molded, F50) | 21.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 67 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, Injection Molded) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, Injection Molded | 11 | % | |
| Break, Injection Molded | 430 | % | |
| Flexural Modulus (Injection Molded) | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 16 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 130 | °C | ISO 306/A120 |
| Oxidation Induction Time - Injection Molded (200°C) | 8.0 | min | EN 728 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3W Q601 | BASF Corporation | Nylon 66 | Ultramid® |
| Epolene® E-16 | Westlake Chemical Corporation | LDPE | Epolene® |
| Sylvin 802-88 Red 648 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TECACOMP® PA6 CF30 black 3553 | Ensinger GmbH | Nylon 6 | TECACOMP® |
| CYCOLAC™ DL100LG resin | SABIC Innovative Plastics Europe | ABS | CYCOLAC™ |