AKROMID® A3 1 S3 black (2768)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 01tQ0x_AKROMID-A3-1-S3-black-2768-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 1 S3 black (2768) is an unreinforced, heat stabilised, dry impact resistant polyamide 6.6. Applications are connecting and fixing systems, used are elevated temperatures in the automotive and elctro industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.11 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 52.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.1 | -- | % | |
| Flow | 2.0 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.5 | -- | % | ISO 1110 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 125 | 65.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2600 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 68.0 | 42.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.4 | -- | % | |
| Break | > 25 | > 50 | % | |
| Flexural Modulus 1 | 2100 | 1000 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | |||
| -- 3 | 65.0 | -- | MPa | |
| -- | 81.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 11 | 28 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 11 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 194 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 260 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Standard Flexural Stress |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PC/PBT PC/PBTQX7008 | Nexus Resin Group, LLC. | PC+PBT | NEXUS PC/PBT |
| FERREX® GPP20CF99HB WHITE | Ferro Corporation | PP Homopolymer | FERREX® |
| Durethan® BKV 40 H2.0 901510 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |
| ICORENE® 3560 DW | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| MAJORIS HG264X - 1298 | AD majoris | PP, Unspecified | MAJORIS |