TRIBOCOMP® PA6 CF30 TS0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 00yf3w_TRIBOCOMP-PA6-CF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PA6 CF30 TS0 is a polyamide 6 (nylon 6) product, which contains 15% ptfe fiber and 30% carbon fiber reinforced materials. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 19500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 200 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 17000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 290 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 215 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.1E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.51 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ASTM D257 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 230 - 270 | °C | |
| Middle Temperature | 235 - 280 | °C | |
| Front Temperature | 235 - 280 | °C | |
| Nozzle Temperature | 235 - 290 | °C | |
| Processing (Melt) Temp | < 320 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ST-16151-05-02 Black | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| Boda BDF-H2751 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Daelim Po1y® 6007LD | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Flontech® FT-1-FM-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| LNP™ THERMOCOMP™ LC004XXP compound | SABIC Innovative Plastics Europe | PEEK | LNP™ THERMOCOMP™ |